Name: HDPE Textured Geomembrane
SKU: 0



+86 18266448692

Products

Deep Expertise in R&D and Manufacturing | International-Standard Quality Control | Customized Solutions | Serving Global Infrastructure and Environmental Initiatives



Location: Home > Products > Geomembrane > HDPE Geomembrane > HDPE Textured Geomembrane

HDPE Textured Geomembrane

Warranty 1 Year
After-sale Service Online technical support
Project Solution Capability total solution for projects
Application Outdoor
Design Style Industrial

International Compliance & Quality

Robust Performance Across All Scenarios

On-Demand Customization

Stable Batch Delivery

WhatsApp : +86 18266448692

Email : admin@hwangmaterial.com

View Quote >

Product Description

Properties	Test Method	Test Value							Testing Frequency (minimum)
Properties	Test Method	0.75 mm	1.00 mm	1.25 mm	1.50 mm	2.00 mm	2.50 mm	3.00 mm	Testing Frequency (minimum)
Thickness (min. ave.) - mm	D 5994	nom. -5%	nom. -5%	nom. -5%	nom. -5%	nom. -5%	nom. -5%	nom. -5%	per roll
• lowest individual for 8 out of 10 values - %		-10	-10	-10	-10	-10	-10	-10
• lowest individual for any of the 10 values - %		-15	-15	-15	-15	-15	-15	-15
Asperity Height mils (min. ave.) - mm	D 7466	0.4	0.4	0.4	0.4	0.4	0.4	0.4	every 2nd roll (1)
Formulated Density (min. ave.) - g/cc	D 1505/D 792	0.94	0.94	0.94	0.94	0.94	0.94	0.94	90,000 kg
Tensile Properties (min. ave.) (2)	D 6693 Type IV	11	15	18	22	29	37	44	9,000 kg
• yield strength - kN/m		8	10	13	16	21	26	32
• break strength - kN/m		12	12	12	12	12	12	12
• yield elongation - %		100	100	100	100	100	100	100
• break elongation - %
Tear Resistance (min. ave.) - N	D 1004	93	125	156	187	249	311	374	20,000 kg
Puncture Resistance (min. ave.) - N	D 4833	200	267	333	400	534	667	800	20,000 kg
Stress Crack Resistance (3) - hr.	D 5397 (App.)	500	500	500	500	500	500	500	per GRI GM10
Carbon Black Content (range) - %	D 4218 (4)	2.0-3.0	2.0-3.0	2.0-3.0	2.0-3.0	2.0-3.0	2.0-3.0	2.0-3.0	9,000 kg
Carbon Black Dispersion	D 5596	note (5)	note (5)	note (5)	note (5)	note (5)	note (5)	note (5)	20,000 kg
Oxidative Induction Time (OIT) (min. ave.) (6)	D 3895	100	100	100	100	100	100	100	90,000 kg
Oxidative Induction Time (OIT) (min. ave.) (6)	D 3895	100	100	100	100	100	100	100
— or —
(b) High Pressure OIT - min.	D 5885	400	400	400	400	400	400	400
Oven Aging at 85°C (6), (7) (a) Standard OIT (min. ave.) - % retained after 90 days	D 5721								per each formulation
	D 3895	55	55	55	55	55	55	55
— or —
(b) High Pressure OIT (min. ave.) - % retained after 90 days	D 5885	80	80	80	80	80	80	80
UV Resistance (8) (a) Standard OIT (min. ave.)	D 7238 D 3895	N.R. (9)	N.R. (9)	N.R. (9)	N.R. (9)	N.R. (9)	N.R. (9)	N.R. (9)	per each formulation
UV Resistance (8) (a) Standard OIT (min. ave.)	D 7238 D 3895	N.R. (9)	N.R. (9)	N.R. (9)	N.R. (9)	N.R. (9)	N.R. (9)	N.R. (9)
— or —	D 5885
(b) High Pressure OIT (min. ave.) - % retained after 1600 hrs (10)	D 5885	50	50	50	50	50	50	50